| MORGAN'S FINE QUARTZ SILICATE-BASED PAINT A1 |
| Silicate-based paint. Water absorption W24: 0.416 kg/sq m.vh Equivalent air thickness Sd: 0.013 mWater vapour permeability V: 67.2 g/sq m.h Water vapour permeability coefficient m : 56 The properties of the Silicate-based paint are well within the limits of standard DIN 4108.3, which determines:W24 < 0.5 ; Sd < 2 m ; W24 x Sd < 0.1 |
|
|
|
|
| MORGAN'S MEDIUM QUARTZ SILICATE-BASED PAINT A 2 |
| Silicate-based paint. Water absorption W24: 0.475 kg/sq m.h Equivalent air thickness Sd: 0.012 mWater vapour permeability V: 65 g/sq m.h Water vapour permeability coefficient m: 52 The properties of the Silicate-based paint are well within the limits of standard DIN 4108.3, which determines:W24 < 0.5 ; Sd < 2 m ; W24 x Sd < 0.1 |
|
|
|
|
| MORGAN'S STANDARD-EFFECT SILICATE COVERING B 2 |
| Silicate covering with particle size resembling normal standard plaster (~ 1 mm). Fine-structured mineral covering for decorating façades, especially for conservation work on façades in historic city centres. It can be treated with Morgan's Siloxanic Glaze E1 for decorative glaze effects. |
|
|
|
|
|
|
|
|
| RENAISSANCE NATURAL PLASTER |
| Plaster formulated with a blend of slow-curing lime putty, select extenders with medium particle size and non film-forming additives in powder. Particularly recommended for decorating exterior and interior walls. Ideal base coat for RINASCIMENTO CALCE NATURALE A SPATOLA if you want the trowel effect. Impervious to mould, fungal and bacterial growth. Features excellent transpirability. |
|
|
|
|
| RENAISSANCE NATURAL BRUSH LIME |
| Paint formulated with a blend of slow-process hydrated lime, natural earth, and non film-forming additives in powder.Particularly suitable for decorating exterior and interior walls.Impervious to mould, fungal and bacterial growth. Can be coloured with inorganic universal colorants.Features excellent transpirability. |
|
|
|
|
| MORGAN’S SILOXANIC GLAZING E1 |
| Water-based acrylic-siloxanic decorative glaze, formulated with self cross-linking elastic acrylic and siloxanic resins dispersed in the vehicle.The product features great water vapour permeability and is water repellent.It is meant as a decorative finish as part of the no-crack elastomeric coating system - with which it is perfectly compatible owing to the elasticity of the acrylic resin used - and as a finish and glaze on MORGAN'S PLASTIC QUARZO EXTRA FINE and MICRON, as well as in the architectural chromatic restoration of exterior façades, and for interior decorating |
|
|
|
|
| Morgan's siloxan |
| Odourless solvent-solution siloxan protective covering for exterior use. Does not block substrate pores, enabling it to breathe. Impervious to weathering. Can be used on substrates with low or high absorption, on light and dark plaster, on exposed brickwork or stone of a sedimentary nature. |
|
|
|
|
| ACRYLIC-SILOXANIC PAINT |
| Top-quality paint for interior and exterior use produced by combining acrylic and siloxanic resins. Features remarkable transpirability, water repellence and outdoor resistance. Does not block the wall's pores, enabling it to breathe. Its high siloxanic resin content means it forms an effective rain barrier.Wet abrasion resistance with UNICHIM method n° 1005: > 10,000 cycles.Capillary water absorption (W24): 0.25 kg/m² Öh.Vapour diffusion resistance (SD): 0.05 metres equivalent.Values W24 and SD refer to the complete coating system made up of a coat of impregnating agent or sealer and two coats of paint. |
|
|
|
|
| ACRYLIC-SILOXANIC COVERING |
| Thick surface coating formulated with special acrylic-siloxanic resins, select extenders with non-spheroidal marble particles between 0.7 and 1 mm in size.Remarkable water repellence and outstanding water vapour permeability (breathability) make this thick covering an ideal topcoat for old or new plaster, producing an extremely attractive non-textured coloured decorative finish.It can be used as the undercoat instead of our MINERAL COMPOUNDING PRIMER (RASANTE MINERALE) to fill any defects in the façade owing to uneven surfaces or irregularities that have formed on old paintwork and coverings.Water absorption W24: 0.5 DIN 52617Equivalent air thickness Sd: 0.1 DIN 18550W24 x Sd : 0.005 DIN 18550 (W24 x Sd < 0.1) |
|